Hydraulic Cylinder Piston Hollow Chrome Plated Rod Bar NSS 500 Hours 42CrMo

Hydraulic Cylinder Piston Hollow Chrome Plated Rod Bar NSS 500 Hours 42CrMo

    • Hydraulic Cylinder Piston Hollow Chrome Plated Rod Bar NSS 500 Hours 42CrMo
    • Hydraulic Cylinder Piston Hollow Chrome Plated Rod Bar NSS 500 Hours 42CrMo
    • Hydraulic Cylinder Piston Hollow Chrome Plated Rod Bar NSS 500 Hours 42CrMo
  • Hydraulic Cylinder Piston Hollow Chrome Plated Rod Bar NSS 500 Hours 42CrMo

    Product Details:

    Place of Origin: CHINA
    Brand Name: DALLAST
    Certification: SGS TUV
    Model Number: Model

    Payment & Shipping Terms:

    Minimum Order Quantity: 1
    Packaging Details: Wooden box
    Delivery Time: 15-25DAYS
    Payment Terms: T/T
    Supply Ability: 100000PCS/YEAR
    Contact Now
    Detailed Product Description
    Material: 45# 42CrMo Color: Black
    NSS: Endure 300;500;800hours Type: Hollow/Solid Rod
    Application Environment: At Sea Or In Harsh Environments Surface Hardness: >HV850

    42CrMo Hydraulic Cylinder Piston Hollow Rods Hard Chrome Plated Steel Bar NSS 500 Hours


    Material :42CrMo

     

    Color :Black

     

    NSS:Endure 300;500;800hours

     

    Type:Hollow/Solid Rod


    Application Environment:At sea or in harsh environments

     

    Surface hardness:>HV860

     

    SURFACE ROUGHNESS:Ra≤0.2 micron and Rt≤2 micro

     

    TOLERANCES ON DIA:ISO f10 on the diameter

     

    Testing Standing une-en iso9227:2017

     

    · Sal solution: 50 (+/- 5) g/l of NaCl. Water is demineralized and salt purity is 99.5%.

    · Environmental temperature: 35 °C.

    · pH of salt solution is 6.8.

    · Volumen of salt solution is 38.4 ml/day.

    · Density of salt solution is 1,030 g/cm3.

    · Spraying is 1.5 (+/- 0.5) ml/h.

    Test Result :NSS can endure 300 hours ;500 hours; 800 hours

     

    SGS NSS Testing Report                       TUV NSSTesting Repopt 

     

     

    Heat treatment

    1.Quenching with fire about 860 °C, placed in furnace box

    2. After quenching, put into the oil tank to cool from the box furnace

    3. After cooling, the first time tempering: tempered at 640 °C and the hardness is controlled at about HRC28-32, the first time tempering cooling is used Water-cooled.

    4. Straightening: The outer circle is controlled by 200 um(0.2mm) ;

    straightening equipment:

    three-roller straightening machine;

    hydraulic straightening machine (multipoint straightening)

    5. The second tempering removes the hard force, the temperature is about 480 °C, and Keep warm for 2 -2.5hours ; release 80% more or less

     

    In the whole crafts process, there are 2 times remove hardening forces: the first remove hardening force in the heat treatment process, hardening force remove is about 80%; the second remove hardening force in the surface treatment process, hardening force remove is about 90%-95%. Therefore, the piston rod is not easily deformed during use or transportation.

     

    CHEMICAL COMPOSITION

     

    Material C% Mn% Si% S% P% V% Cr%
    Ck45 0.42-0.50 0.50-0.80 0.04 0.035 0.035    
    ST52 0.22 1.6 0.55 0.035 0.04    
    20MnV6 0.16-0.22 1.30-1.70 0.10-0.50 0.035 0.035 0.10-0.20  
    42CrMo4 0.38-0.45 0.60-0.90 0.15-0.40 0.03 0.03   0.90-1.20
    40Cr 0.37-0.45 0.50-0.80 0.17-0.37       0.80-1.10

    MECHANCIAL PROPERTIES

    Material T.S N/MM2 Y.S N/MM2 E%(MIN) CHARPY CONDITION
    CK45 610 355 15 >41J NORMALIZE
    CK45 800 630 20 >41J Q + T
    ST52 500 355 22   NORMALIZE
    20MnV6 750 590 12 >40J NORMALIZE
    42CrMo4 980 850 14 >47J Q + T
    40Cr 1000 800 10   Q + T

    Hydraulic Cylinder Piston Hollow Chrome Plated Rod Bar NSS 500 Hours 42CrMo

    Hydraulic Cylinder Piston Hollow Chrome Plated Rod Bar NSS 500 Hours 42CrMo

    Hydraulic Cylinder Piston Hollow Chrome Plated Rod Bar NSS 500 Hours 42CrMo

     